RT Journal Article SR Electronic T1 Failure of Glass Tubing Vials during Lyophilization JF PDA Journal of Pharmaceutical Science and Technology JO PDA J Pharm Sci Technol FD Parenteral Drug Association (PDA) SP 30 OP 38 DO 10.5731/pdajpst.2017.008276 VO 73 IS 1 A1 David R. Machak A1 Gary L. Smay YR 2019 UL http://journal.pda.org/content/73/1/30.abstract AB Lyophilization is a commonly used and often preferred method for preparing certain drug products. In this process, the liquid pharmaceutical product is packaged in glass vials, frozen, and then dried via sublimation at low pressures. One problem that can be encountered during lyophilization is the occasional failure of the glass vial, a condition that will be referred to in this paper as “lyo-breakage.” Lyo-breakage, while relatively rare, can be a serious problem, as it results in lost product, additional costs to remediate any spillage, and inspection time to ensure that all broken vials are discarded. Some companies have suggested that lyo-breakage is related to thermal stress and, subsequently, can be reduced through changes to the thermal properties of the vials. In this paper, we will show that when the most common form of lyo-breakage occurs, the stresses in the glass are caused by an internal force from product expansion during freezing and not due to thermal stress from processing temperatures.LAY ABSTRACT: Lyophilization, or freeze drying, is often the preferred method for preparing certain drug products following manufacture. In this process, the liquid pharmaceutical product is packaged in a small glass cylindrical container called a vial, frozen, and then dried at low pressures. One problem that can be encountered during lyophilization is the occasional failure of the glass vial. While relatively rare, this failure can result in lost drug product, additional costs to clean up any spillage, and increased inspection time to ensure that all broken vials are discarded. The data presented in this paper demonstrate that when the most common form of lyophilization-associated breakage occurs, the stresses in the glass are caused by an internal force from drug product expansion during freezing and not due to thermal stress on the glass from processing temperatures.