T0 | AC | RT5 | RT12 | RT24 | AT12 | AT24 | AT36 | |||
---|---|---|---|---|---|---|---|---|---|---|
Al2O3 | Glass A | Average | <LoQ | 1.14 | <LoQ | <LoQ | 0.08 | 0.26 | 0.26 | 0.30 |
SD | NA | 0.10 | NA | NA | 0.01 | 0.04 | 0.06 | 0.07 | ||
Glass B | Average | <LoQ | 0.98 | <LoQ | <LoQ | 0.05 | 0.40 | 0.35 | 0.38 | |
SD | NA | 0.32 | NA | NA | 0.01 | 0.10 | 0.09 | 0.13 | ||
B2O3 | Glass A | Average | <LoQ | 4.11 | 1.29 | 1.63 | 2.28 | 4.44 | 6.24 | 7.06 |
SD | NA | 0.25 | 0.12 | 0.21 | 0.27 | 0.30 | 0.48 | 0.68 | ||
Glass B | Average | <LoQ | 8.55 | 2.97 | 4.22 | 5.62 | 9.55 | 13.23 | 13.83 | |
SD | NA | 0.73 | 0.91 | 1.07 | 1.50 | 3.34 | 4.70 | 4.33 | ||
SiO2 | Glass A | Average | <LoQ | 21.85 | 3.43 | 4.15 | 7.15 | 14.03 | 18.37 | 20.73 |
SD | NA | 1.08 | 0.24 | 0.40 | 0.61 | 1.33 | 1.20 | 2.01 | ||
Glass B | Average | <LoQ | 24.28 | 5.78 | 7.29 | 10.82 | 22.18 | 28.28 | 30.18 | |
SD | NA | 2.81 | 1.73 | 1.86 | 2.70 | 7.86 | 10.70 | 9.57 | ||
CaO | Glass A | Average | 0.43 | 1.24 | 0.30 | 0.41 | 0.54 | 1.09 | 1.21 | 1.37 |
SD | 0.17 | 0.13 | 0.02 | 0.04 | 0.04 | 0.09 | 0.07 | 0.14 | ||
Glass B | Average | 0.43 | 0.77 | 0.25 | 0.34 | 0.46 | 0.81 | 0.99 | 1.05 | |
SD | 0.15 | 0.05 | 0.05 | 0.07 | 0.11 | 0.20 | 0.25 | 0.24 |
↵a The concentration of the oxides is reported in mg/L. LoQ Al, B, Ca = 0.05; LoQ Si = 0.2. NA, not applicable; RT, real time; AT, accelerated time; AC, autoclave cycle.